High Stretch Fabric AA403 is a versatile fabric that can be used in a variety of applications, including geometric designs, trade shows, grand format prints, and table stretch projects. The fabric is made of 85% polyester and 15% spandex, which provide excellent elasticity. The warp-knitted 2 bar construction using 75D*75D yarn ensures the fabric is durable enough to withstand multiple uses. It has a weight of 75D*75D and a thickness of 600±50μm with a high opacity of 85% or more. The fabric has a whiteness value of 165±10, color value of L:88.0±2.0, a:8.5±2.0, b:-20.0±2.0, and elasticity ranging between Warp:(10±3)% and Weft:(30±5)%. With a recommended fixation temperature of 190-200℃, it has a yellowing temperature of ≥210℃ and shrinkage of less than or equal to 2%.
| Base Material | 100% polyester | DIN 60001, ASTM D7641 |
| Yarn | 75D*75D | DIN EN 2060, ASTM D1907 |
| Weave Method | Warp-knitted 2 bar | --- |
| Weight | 255±10gsm | ISO536 |
| Thickness | 600±50μm | ISO534 |
| Opacity | ≥85% | ISO2471 |
| Whiteness | 165±10 | ISO11475 |
| Color | L: 88.0±2.0; a: 8.5±2.0; b: -20.0±2.0 | --- |
| Gloss[60°] | 4±2 | --- |
| Elasticity | Warp:(10±3)% Weft:(30±5)% | Length*Width=200*50mm,Speed=100mm/min,Tension=20N |
| Shrinkage | ≤2% | 200°C，45s |
| Yellowing △E | ≤2 | 200°C，45s |
| Flame Resistance | DIN 4102-1 B1, NFPA 701 | DIN 4102-1 B1, NFPA 701 |
| Recommend Fixation Temperature | 190-200℃,45s | --- |
| Yellowing Temperature | ≥210℃ | SUPRKC REX-C400,30s |
Size
| Size | |||
| Width | 1.60 m/2.60 m/3.20 m | Standard | DIN EN ISO 3759, ASTM D751-2006 |
| Length | 50m | Standard | DIN EN ISO 3759, ASTM D751-2006 |
Compatible Inks
| Compatible Inks | |
| Dye-sub Transfer | Dye-sub Direct |